Ultem PEI 1000-1000

2015-12-21 13:58

Ultem PEI 1000
Not enhanced. DTUL (deflection temperature under load): 392F (200C), 264 psi. UL94 V-0 / 5V rated. In 1000-1000ONLY--USP Class VI, FDA food contact appliances and tripartite (ISO 10993-1 revision).
machining

Extrusion-USA
Note: Mold release grades (numbers ending with R), due to the inclusion of mold release agents, fouling and / or die biting can occur.
Dry for 4 hours at 300F
Temperature (F)
Melt 625-675
Back 1 615-660
Mid Section 625-675
Front 625-675
Die pressure (psi) 1200-7000
Screw design Compression ratio: 1.8 to 2.8: 1.0
L / D (length-diameter ratio): 16 ~ 24: 1
Screw speed (rpm) 10-70
Cleaning: use HDPE or undried polycarbonate
Batch Extrusion Blow Molding-USA
Intermittent Extrusion Blow Molding WARNING: Do not use low-melting styrene or acrylic resin cleaners.
Group: ULT-IEXTBM-01 Unit Drying temperature deg F 280-300
Drying time (basic) hr 4-6
Drying time (max.) Hr 24
Moisture content, max% 0.01-0.02
Melt temperature (parison) deg F 610-675
Barrel-Area 1 deg F 615-660
Barrel-Area 2 deg F 625-675
Barrel-Area 3 deg F 625-675
Barrel-Area 4 deg F 625-675
Socket-Area 5 deg F 625-675
Head-Area 6-Upper deg F 625-675
Head-Area 7-Bottom deg F 625-675
Head-Area 8-Die Head deg F 620-675
Mold temperature deg F 150-350
Screw speed rpm 10-70
Screws with L / D (length to diameter ratio) of 16 to 24/1 and compression ratio of 1.8 to 2.5 / 1.0.
30% of recycled materials have been successfully reprocessed.
Use 0.030-0.035 MFR HDPE or high viscosity polycarbonate cleaner.

Injection-USA
Processing group: ULT-IM-01
Note: Melt temperatures above 720F and / or excessive residence time at this temperature may affect color stability.
Drying time 4-6 hr
Drying temperature 300 deg F
Maximum drying time 24 hr
Moisture content (range) 0.02%
Melt temperature 660-750 deg F
Nozzle temperature 650-750 deg F
Front temperature 650-750 deg F
Mid-range temperature 640-750 deg F
Rear temperature 630-750 deg F
Mold temperature 275-325 deg F
Back pressure 50-100 psig
Screw speed 40-70 rpm
Barrel injection volume 40-60%
Clamping force tonnage 3-5 ton / in2
Mold exhaust groove depth 0.001-0.003 in

Not enhanced. DTUL (deflection temperature under load): 392F (200C), 264 psi. UL94 V-0 / 5V rated. In 1000-1000ONLY--USP Class VI, FDA food contact appliances and tripartite (ISO 10993-1 revision).
performance

mechanical
performance Typical data unit method
Tensile Strength, Yield, Type I, 0.125 " 15200 psi ASTM D 638
Tensile Extension, Yield, Type I 0.125 " 7.0 % ASTM D 638
Tensile Extension, Break, Type I 0.125 " 60.0 % ASTM D 638
Flexural Strength, Yield, 0.125 " 22000 psi ASTM D 790
Flexural Modulus, 0.125 " 480000 psi ASTM D 790
Compressive strength 21900 psi ASTM D 695
Compression modulus 480000 psi ASTM D 695
Shear strength 15000 psi ASTM D 732
Hardness, Rockwell M 109 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg / 1000cy ASTM D 1044
Shock
performance Typical data unit method
Izod impact value, no gap, 73F 25.0 ft-lb / in ASTM D 4812
Izod impact value, notch, 73F 1.0 ft-lb / in ASTM D 256
Gardner Shock, 73F 27 ft-lbs ASTM D 3029
heat
performance Typical data unit method
Vicat softening temperature, Class B 426 deg F ASTM D 1525
HDT (thermal distortion temperature), 66 psi, 0.250 ", unannealed 410 deg F ASTM D 648
HDT (thermal distortion temperature), 264 psi, 0.250 ", unannealed 392 deg F ASTM D 648
Thermal conductivity 0.22 W / mC ASTM C 177
CTE (Coefficient of Thermal Expansion), flow, 0F ~ 300F 3 E-5 in / in-F ASTM E 831
CTE (Coefficient of Thermal Expansion), xflow, 0F ~ 300F 3 E-5 in / in-F ASTM E 831
Heat index 170 deg C UL 746B
Thermal index, mechanical shock performance 170 deg C UL 746B
Thermal index, non-mechanical impact performance 170 deg C UL 746B
physical
performance Typical data unit method
Specific gravity, solid 1.27 - ASTM D 792
Water absorption, 24 hours @ 73F 0.250 % ASTM D 570
Water absorption, equilibrium, 73F 1.25 % ASTM D 570
Mold Shrinkage, flow, 0.125 " 5-7 in / in E-3 ASTM D 955
Melt flow rate, nominal, 337C 6.6 kgf 8.9 g / 10 min ASTM D 1238
Poisson's ratio 0.36 - ASTM D 638
Electricity
performance Typical data unit method
Volume resistivity 1 E17 ohm-cm ASTM D 257
Dielectric strength, in air, 62 mils 831 V / mil ASTM D 149
Dielectric strength, in oil, 62 mils 710 V / mil ASTM D 149
Dielectric strength, in oil, 125 mils 500 V / mil ASTM D 149
Dielectric constant, 100 Hz 3.15 - ASTM D 150
Dielectric constant, 1 kHz 3.15 - ASTM D 150
Loss factor, 100 Hz 0.0015 - ASTM D 150
Loss factor, 1 kHz 0.0012 - ASTM D 150
Loss factor, 2450 MHz 0.0025 - ASTM D 150
Flame characteristics
performance Typical data unit method
UL file number, USA E121562 - -
V-0 rating (test thickness) 0.016 inch UL 94
5VA rating (test thickness) 0.075 inch UL 94
CSA (see documentation for complete list) LS88480 Document number CSA LISTED
Oxygen index (LOI) 47.0 % ASTM D 2863
NBS smoke density, flame burning, Ds 4 min 0.7 - ASTM E 662
NBS smoke density, flame burning, Dmax 20 min 30.0 - ASTM E 662 Ultem PEI 1000 Physical properties are not enhanced. DTUL (deflection temperature under load): 392F (200C), 264 psi. UL94 V-0 / 5V rated. In 1000-1000ONLY--USP Class VI, FDA food contact appliances and tripartite (ISO 10993-1 revision).
machining
Extrusion-USA
Note: Mold release grades (numbers ending with R), due to the inclusion of mold release agents, fouling and / or die biting.
Dry for 4 hours at 300F
Temperature (F)
Melt 625-675
Back 1 615-660
Mid Section 625-675
Front 625-675
Die pressure (psi) 1200-7000
Screw design Compression ratio: 1.8 to 2.8: 1.0
L / D (length-diameter ratio): 16 ~ 24: 1
Screw speed (rpm) 10-70
Cleaning: use HDPE or undried polycarbonate
Batch Extrusion Blow Molding-USA
Intermittent extrusion blow molding
Warning: Do not use low-melting styrene or acrylic resin cleaner.
Group: ULT-IEXTBM-01 Unit
Drying temperature deg F 280-300
Drying time (basic) hr 4-6
Drying time (max.) Hr 24
Moisture content, max% 0.01-0.02
Melt temperature (parison) deg F 610-675
Barrel-Area 1 deg F 615-660
Barrel-Area 2 deg F 625-675
Barrel-Area 3 deg F 625-675
Barrel-Area 4 deg F 625-675
Socket-Area 5 deg F 625-675
Head-Area 6-Upper deg F 625-675
Head-Area 7-Bottom deg F 625-675
Head-Area 8-Die Head deg F 620-675
Mold temperature deg F 150-350
Screw speed rpm 10-70
Screws with L / D (length to diameter ratio) of 16 to 24/1 and compression ratio of 1.8 to 2.5 / 1.0.
30% of recycled materials have been successfully reprocessed.
Use 0.030-0.035 MFR HDPE or high viscosity polycarbonate cleaner.

Injection-USA
Processing group: ULT-IM-01
Note: Melt temperatures above 720F and / or excessive residence time at this temperature may affect color stability.
Drying time 4-6 hr
Drying temperature 300 deg F
Maximum drying time 24 hr
Moisture content (range) 0.02%
Melt temperature 660-750 deg F
Nozzle temperature 650-750 deg F
Front temperature 650-750 deg F
Mid-range temperature 640-750 deg F
Rear temperature 630-750 deg F
Mold temperature 275-325 deg F
Back pressure 50-100 psig
Screw speed 40-70 rpm
Barrel injection volume 40-60%
Clamping force tonnage 3-5 ton / in2
Mold exhaust groove depth 0.001-0.003 in
Not enhanced. DTUL (deflection temperature under load): 392F (200C), 264 psi. UL94 V-0 / 5V rated. In 1000-1000ONLY--USP Class VI, FDA food contact appliances and tripartite (ISO 10993-1 revision).
performance
mechanical
performance Typical data unit method
Tensile Strength, Yield, Type I, 0.125 " 15200 psi ASTM D 638
Tensile Extension, Yield, Type I 0.125 " 7.0 % ASTM D 638
Tensile Extension, Break, Type I 0.125 " 60.0 % ASTM D 638
Flexural Strength, Yield, 0.125 " 22000 psi ASTM D 790
Flexural Modulus, 0.125 " 480000 psi ASTM D 790
Compressive strength 21900 psi ASTM D 695
Compression modulus 480000 psi ASTM D 695
Shear strength 15000 psi ASTM D 732
Hardness, Rockwell M 109 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg / 1000cy ASTM D 1044
Shock
performance Typical data unit method
Izod impact value, no gap, 73F 25.0 ft-lb / in ASTM D 4812
Izod impact value, notch, 73F 1.0 ft-lb / in ASTM D 256
Gardner Shock, 73F 27 ft-lbs ASTM D 3029
heat
performance Typical data unit method
Vicat softening temperature, Class B 426 deg F ASTM D 1525
HDT (thermal distortion temperature), 66 psi, 0.250 ", unannealed 410 deg F ASTM D 648
HDT (thermal distortion temperature), 264 psi, 0.250 ", unannealed 392 deg F ASTM D 648
Thermal conductivity 0.22 W / mC ASTM C 177
CTE (Coefficient of Thermal Expansion), flow, 0F ~ 300F 3 E-5 in / in-F ASTM E 831
CTE (Coefficient of Thermal Expansion), xflow, 0F ~ 300F 3 E-5 in / in-F ASTM E 831
Heat index 170 deg C UL 746B
Thermal index, mechanical shock performance 170 deg C UL 746B
Thermal index, non-mechanical impact performance 170 deg C UL 746B
physical
performance Typical data unit method
Specific gravity, solid 1.27 - ASTM D 792
Water absorption, 24 hours @ 73F 0.250 % ASTM D 570
Water absorption, equilibrium, 73F 1.25 % ASTM D 570
Mold Shrinkage, flow, 0.125 " 5-7 in / in E-3 ASTM D 955
Melt flow rate, nominal, 337C 6.6 kgf 8.9 g / 10 min ASTM D 1238
Poisson's ratio 0.36 - ASTM D 638
Electricity
performance Typical data unit method
Volume resistivity 1 E17 ohm-cm ASTM D 257
Dielectric strength, in air, 62 mils 831 V / mil ASTM D 149
Dielectric strength, in oil, 62 mils 710 V / mil ASTM D 149
Dielectric strength, in oil, 125 mils 500 V / mil ASTM D 149
Dielectric constant, 100 Hz 3.15 - ASTM D 150
Dielectric constant, 1 kHz 3.15 - ASTM D 150
Loss factor, 100 Hz 0.0015 - ASTM D 150
Loss factor, 1 kHz 0.0012 - ASTM D 150
Loss factor, 2450 MHz 0.0025 - ASTM D 150
Flame characteristics
performance Typical data unit method
UL file number, USA E121562 - -
V-0 rating (test thickness) 0.016 inch UL 94
5VA rating (test thickness) 0.075 inch UL 94
CSA (see documentation for complete list) LS88480 Document number CSA LISTED
Oxygen index (LOI) 47.0 % ASTM D 2863
NBS smoke density, flame burning, Ds 4 min 0.7 - ASTM E 662
NBS smoke density, flame burning, Dmax 20 min 30.0 - ASTM E 662

Previous: No more
Next: Ultem PEI 1010-1000

Working with Plastic Engine

You will get more mature professional engineering plastics supply services. We put customers first, and also actively challenge, and strive to present the best service quality to our customers.

Engineering Plastics Hotline:

400-6700-720
020-38937005

About Plastic Engine:
AG真人网 真人斗牛app 电玩竞技游戏 真人斗牛app 电玩游戏平台 电玩竞技游戏 皇冠体育官网 博狗直营