Position: 2元彩票 > Products > Ultem PEI > ULTEM > PEI >

Ultem PEI HU1000-1H1000

2015-12-21 14:23

Ultem PEI HU1000
Physical properties
Rating
Unit system
Test Methods
proportion
1.27
g / cm3
, ISO 1183 ASTM D792 , ISO 1183
(337°C/6.6 kg) Melt flow rate (melt flow rate) (337 ° C / 6.6 kg)
9.0
g / 10 min
ASTM D1238
(220°C/5.0 kg) Melt Volume Flow Rate (MVR) (220 ° C / 5.0 kg)
13.0
cm3 / 10min
ISO 1133
(3.20 mm) Shrinkage-Flow (3.20 mm)
0.50 to 0.70
%
Internal method
Water absorption
24 hr
0.25
%
ASTM D570
Saturated, 23 ° C
1.3
%
ISO 62
Equilibrium, 23 ° C
1.3
%
ASTM D570
Equilibrium, 23 ° C, 50% RH
0.70
%
ISO 62

Mechanical behavior
Rating
Unit system
Test Methods
Tensile modulus
-2
3580
MPa
ASTM D638
-
3200
MPa
ISO 527-2 / 1
tensile strength
Yield 3
110
MPa
ASTM D638
yield
105
MPa
ISO 527-2 / 5
Break 3
90.0
MPa
ASTM D638
fracture
85.0
MPa
ISO 527-2 / 5
Elongation
Yield 3
7.0
%
ASTM D638
yield
6.0
%
ISO 527-2 / 5
Break 3
60
%
ASTM D638
fracture
60
%
ISO 527-2 / 5
Flexural modulus
50.0 mm span 4
3440
MPa
ASTM D790
-5
3300
MPa
ISO 178
Bending stress
, 6 -5 , 6
160
MPa
ISO 178
Yield, 50.0 mm span 4
173
MPa
ASTM D790
Impact performance
Rating
Unit system
Test Methods
(23°C) Notched impact strength of simply supported beam 7 (23 ° C)
4.0
kJ / m2
ISO 179 / 1eA
Notched Izod Impact Strength
-30 ° C
55
J / m
ASTM D256
23 ° C
53
J / m
ASTM D256
-30 ° C 8
6.0
kJ / m2
ISO 180 / 1A
23 ° C 8
6.0
kJ / m2
ISO 180 / 1A
(23°C) Unnotched Izod Impact (23 ° C)
1300
J / m
ASTM D4812

Thermal performance
Rating
Unit system
Test Methods
Thermal deformation temperature under load
1.8 MPa, unannealed, 6.40 mm
201
° C
ASTM D648
1.8 MPa, unannealed, 64.0 mm span 9
215
° C
ISO 75-2 / Af
Vicat softening temperature
-
219
° C
ASTM D1525 10
-
215
° C
ISO 306 / B50
-
211
° C
ISO 306 / B120
Linear thermal expansion coefficient
Flow: -20 to 150 ° C
5.6E-5
cm / cm / ° C
ASTM E831
Flow: -40 to 40 ° C
5.0E-5
cm / cm / ° C
ISO 11359-2
Horizontal: -20 to 150 ° C
5.4E-5
cm / cm / ° C
ASTM E831
Horizontal: -40 to 40 ° C
5.0E-5
cm / cm / ° C
ISO 11359-2

Electrical performance
Rating
Unit system
Test Methods
Volume resistivity
1.0E + 17
ohmcm
ASTM D257
Dielectric strength
ASTM D149
1.60 mm, in Air
33
kV / mm
1.60 mm, in Oil
28
kV / mm
(1 kHz) Dielectric Constant (1 kHz)
3.15
ASTM D150
Dissipation factor
ASTM D150
1 kHz
1.3E-3
2.45 GHz
2.5E-3
Arc resistance 11
PLC 5
ASTM D495
Compared with tracking resistance index (CTI)
PLC 4
UL 746
High Arc Combustion Index (HAI)
PLC 3
UL 746
High Voltage Arc Tracking Rate (HVTR)
PLC 2
UL 746
Hot Wire Ignition (HWI)
PLC 1
UL 746
Flammability
Rating
Unit system
Test Methods
Limiting oxygen index
47
%
ASTM D2863
NBS Smoke Density-Flaming, Ds, 4 min
0.700
ASTM E662

injection
Rating
Unit system
Drying temperature
149
° C
Drying time
4.0 to 6.0
hr
Drying time, max.
twenty four
hr
Recommended maximum moisture content
0.020
%
Recommended injection volume
40 to 60
%
Barrel rear temperature
332 to 399
° C
Central temperature of barrel
338 to 399
° C
Barrel front temperature
343 to 399
° C
Nozzle temperature
343 to 399
° C
Processing (melt) temperature
349 to 399
° C
Mold temperature
135 to 163
° C
Back pressure
0.345 to 0.689
MPa
Screw speed
40 to 70
rpm
Vent hole depth
0.025 to 0.076
mm

Working with Plastic Engine

You will get more mature professional engineering plastics supply services. We put customers first, and also actively challenge, and strive to present the best service quality to our customers.