Ultem PEI HU1010-1H1000

2015-12-21 14:22

Ultem PEI HU1010, physical properties
Physical properties Rating Unit system Test Methods
proportion 1.27 g / cm3 ASTM D792, ISO 1183
Melt flow rate (melt flow rate) (337 ° C / 6.6 kg) 18 g / 10 min ASTM D1238
Melt Volume Flow Rate (MVR) (220 ° C / 5.0 kg) 25.0 cm3 / 10min ISO 1133
Shrinkage-Flow (3.20 mm) 0.50 to 0.70 % Internal method
Water absorption ISO 62
Saturated, 23 ° C 1.3 %
Equilibrium, 23 ° C, 50% RH 0.70 %
Mechanical behavior Rating Unit system Test Methods
Tensile modulus
-2 3580 MPa ASTM D638
- 3200 MPa ISO 527-2 / 1
tensile strength
Yield 3 110 MPa ASTM D638
yield 105 MPa ISO 527-2 / 5
Break 3 105 MPa ASTM D638
fracture 85.0 MPa ISO 527-2 / 5
Elongation
Yield 3 7.0 % ASTM D638
yield 6.0 % ISO 527-2 / 5
Break 3 60 % ASTM D638
fracture 60 % ISO 527-2 / 5
Flexural modulus
50.0 mm span 4 3420 MPa ASTM D790
100 mm span 5 3520 MPa ASTM D790
-6 3300 MPa ISO 178
Bending stress
-6, 7 160 MPa ISO 178
Yield, 50.0 mm span 4 174 MPa ASTM D790
Yield, 100 mm span 5 165 MPa ASTM D790
Taber abrasion resistance (1000 Cycles, 1000 g, CS-17 runner) 10.0 mg ASTM D1044
Impact performance Rating Unit system Test Methods
Notched impact strength of simply supported beam 8 (23 ° C) 3.0 kJ / m2 ISO 179 / 1eA
Notched Izod Impact Strength
-30 ° C 35 J / m ASTM D256
23 ° C 32 J / m ASTM D256
-30 ° C 9 5.0 kJ / m2 ISO 180 / 1A
23 ° C 9 5.0 kJ / m2 ISO 180 / 1A
Unnotched Izod Impact (23 ° C) 1300 J / m ASTM D4812
Dart impact with measuring instrument (23 ° C, Total Energy) 33.0 J ASTM D3763
Drop weight impact (23 ° C) 33.9 J ASTM D3029

Thermal performance Rating Unit system Test Methods
Thermal deformation temperature under load
1.8 MPa, unannealed, 6.40 mm 199 ° C ASTM D648
1.8 MPa, unannealed, 64.0 mm span 10 193 ° C ISO 75-2 / Af
Vicat softening temperature
- 219 ° C ASTM D1525 11
- 211 ° C ISO 306 / B50
- 212 ° C ISO 306 / B120
Linear thermal expansion coefficient
Flow: -20 to 150 ° C 5.6E-5 cm / cm / ° C ASTM E831
Flow: -40 to 40 ° C 5.0E-5 cm / cm / ° C ISO 11359-2
Horizontal: -40 to 40 ° C 5.0E-5 cm / cm / ° C ASTM E831, ISO 11359-2
Electrical performance Rating Unit system Test Methods
Volume resistivity 1.0E + 17 ohmcm ASTM D257
Dielectric strength ASTM D149
1.60 mm, in Air 33 kV / mm
1.60 mm, in Oil 28 kV / mm
Dielectric Constant (1 kHz) 3.15 ASTM D150
Dissipation factor ASTM D150
1 kHz 1.3E-3
2.45 GHz 2.5E-3
Arc resistance 12 PLC 5 ASTM D495
Compared with tracking resistance index (CTI) PLC 4 UL 746
High Arc Combustion Index (HAI) PLC 3 UL 746
High Voltage Arc Tracking Rate (HVTR) PLC 2 UL 746
Hot Wire Ignition (HWI) PLC 1 UL 746
Flammability Rating Unit system Test Methods
UL flame retardant rating UL 94
0.711 mm V-2
V-0
3.00 mm 5VA
Limiting oxygen index 44 % ASTM D2863

injection Rating Unit system
Drying temperature 149 ° C
Drying time 4.0 to 6.0 hr
Drying time, max. twenty four hr
Recommended maximum moisture content 0.020 %
Recommended injection volume 40 to 60 %
Barrel rear temperature 332 to 399 ° C
Central temperature of barrel 338 to 399 ° C
Barrel front temperature 343 to 399 ° C
Nozzle temperature 343 to 399 ° C
Processing (melt) temperature 349 to 399 ° C
Mold temperature 135 to 163 ° C
Back pressure 0.345 to 0.689 MPa
Screw speed 40 to 70 rpm
Vent hole depth 0.025 to 0.076 mm

Working with Plastic Engine

You will get more mature professional engineering plastics supply services. We put customers first, and also actively challenge, and strive to present the best service quality to our customers.

Engineering Plastics Hotline:

400-6700-720
020-38937005

About Plastic Engine:
AG真人网 真人斗牛app 电玩竞技游戏 真人斗牛app 电玩游戏平台 电玩竞技游戏 皇冠体育官网 博狗直营