cycoloy pc / abs-CH6410-701

2015-12-16 14:59

Cycoloy PC / ABS CH6410-701

CH6410 is a high-heat, impact-improved PC resin. It is flame-retardant without bromine and chlorine, with color restrictions.

Property
(1) TYPICAL PROPERTIES (1)
MECHANICAL
Value Unit Standard
Tensile Stress, yld, Type I, 50 mm / min
640
kgf / cm²
ASTM D 638
Tensile Stress, brk, Type I, 50 mm / min
550
kgf / cm²
ASTM D 638
Tensile Strain, yld, Type I, 50 mm / min
5.5
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm / min
88
%
ASTM D 638
Tensile Modulus, 50 mm / min
25900
kgf / cm²
ASTM D 638
Flexural Stress, yld, 1.3 mm / min, 50 mm span
970
kgf / cm²
ASTM D 790
Flexural Modulus, 1.3 mm / min, 50 mm span
26500
kgf / cm²
ASTM D 790
Tensile Stress, yield, 50 mm / min
63
MPa
ISO 527
Tensile Stress, break, 50 mm / min
55
MPa
ISO 527
Tensile Strain, yield, 50 mm / min
5
%
ISO 527
Tensile Strain, break, 50 mm / min
95
%
ISO 527
Tensile Modulus, 1 mm / min
2300
MPa
ISO 527
Flexural Stress, yield, 2 mm / min
90
MPa
ISO 178
Flexural Modulus, 2 mm / min
2400
MPa
ISO 178
Hardness, H358 / 30
100
MPa
ISO 2039-1
IMPACT
Value Unit Standard
Izod Impact, notched, 23 ° C
92
cm-kgf / cm
ASTM D 256
Instrumented Impact Total Energy, 23 ° C
740
cm-kgf
ASTM D 3763
Izod Impact, notched 80 * 10 * 4 + 23 ° C
50
kJ / m²
ISO 180 / 1A
Izod Impact, notched 80 * 10 * 4 0 ° C
19
kJ / m²
ISO 180 / 1A
Izod Impact, notched 80 * 10 * 4 -30 ° C
15
kJ / m²
ISO 180 / 1A
Charpy 23 ° C, V-notch Edgew 80 * 10 * 4 sp = 62mm
55
kJ / m²
ISO 179 / 1eA
Charpy -30 ° C, V-notch Edgew 80 * 10 * 4 sp = 62mm
15
kJ / m²
ISO 179 / 1eA
THERMAL
Value Unit Standard
HDT, 0.45 MPa, 3.2 mm, unannealed
127
° C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
118
° C
ASTM D 648
CTE, -40 ° C to 40 ° C, flow
7.74E-05
1 / ° C
ASTM E 831
CTE, -40 ° C to 40 ° C, xflow
5.94E-05
1 / ° C
ASTM E 831
CTE, 23 ° C to 60 ° C, flow
7.E-05
1 / ° C
ISO 11359-2
CTE, 23 ° C to 60 ° C, xflow
7.E-05
1 / ° C
ISO 11359-2
Ball Pressure Test, 125 ° C +/- 2 ° C
PASSES
-
IEC 60695-10-2
Vicat Softening Temp, Rate B / 50
134
° C
ISO 306
Vicat Softening Temp, Rate B / 120
135
° C
ISO 306
HDT / Be, 0.45MPa Edgew 120 * 10 * 4 sp = 100mm
126
° C
ISO 75 / Be
HDT / Ae, 1.8 MPa Edgew 120 * 10 * 4 sp = 100mm
113
° C
ISO 75 / Ae
PHYSICAL
Value Unit Standard
Specific Gravity
1.19
-
ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2)
0.05-0.07
%
SABIC Method
Mold Shrinkage, flow, 3.2 mm
0.4-0.5
%
SABIC Method
Melt Flow Rate, 260 ° C / 2.16 kgf
6.3
g / 10 min
ASTM D 1238
Density
1.2
g / cm³
ISO 1183
Melt Volume Rate, MVR at 260 ° C / 5.0 kg
16
cm³ / 10 min
ISO 1133
ELECTRICAL
Value Unit Standard
Volume Resistivity
> 1.E + 15
Ohm-cm
IEC 60093
Surface Resistivity, ROA
> 1.E + 15
Ohm
IEC 60093
Dielectric Strength, in oil, 3.2 mm
18
kV / mm
IEC 60243-1
Relative Permittivity, 50/60 Hz
2.7
-
IEC 60250
Relative Permittivity, 1 MHz
2.7
-
IEC 60250
Dissipation Factor, 50/60 Hz
0.001
-
IEC 60250
Dissipation Factor, 1 MHz
0.01
-
IEC 60250
Comparative Tracking Index
225
V
IEC 60112
FLAME CHARACTERISTICS
Value Unit Standard
UL Recognized, 94V-1 Flame Class Rating (3)
0.99
mm
UL 94
UL Recognized, 94V-0 Flame Class Rating (3)
1.49
mm
UL 94
Parameter
Injection Molding
Value Unit
Drying Temperature
90-100
° C
Drying Time
twenty four
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
270-300
° C
Nozzle Temperature
265-300
° C
Front-Zone 3 Temperature
265-300
° C
Middle-Zone 2 Temperature
260-300
° C
Rear-Zone 1 Temperature
260-300
° C
Mold Temperature
60-90
° C
Back Pressure
0.3-0.7
MPa
Screw Speed
40-70
rpm
Shot to Cylinder Size
40-80
%
Vent Depth
0.038-0.076
mm

Working with Plastic Engine

You will get more mature professional engineering plastics supply services. We put customers first, and also actively challenge, and strive to present the best service quality to our customers.

Engineering Plastics Hotline:

400-6700-720
020-38937005

About Plastic Engine:
AG真人网 真人斗牛app 电玩竞技游戏 真人斗牛app 电玩游戏平台 电玩竞技游戏 皇冠体育官网 博狗直营