cycoloy pc / abs-C7230P-BK1C304

2015-12-16 15:12

Physical properties data
proportion 1.30 g / cc 1.30 g / cc
density 1.30 g / cc 1.30 g / cc
Equilibrium moisture absorption 0.0400% 0.0400%
Water absorption at saturation 0.0900% 0.0900%

Linear molding shrinkage, flow 0.00250-0.00350 cm / cm 0.00250-0.00350 cm / cm

Melt flow 9.00 g / 10 min 9.00 g / 10 minutes

13.0 g / 10 min 13.0 g / 10 min

Mechanical properties Metric male
Tensile breaking strength 35.0 MPa 35.0 MPa
45.0 MPa 45.0 MPa
Tensile strength 55.0 MPa 55.0 MPa
58.0 MPa 58.0 MPa
Elongation at break 30.0% 30.0%
32.0% 32.0%
Yield elongation 3.80% 3.80%
4.00% 4.00%
Tensile modulus 5.20 GPa 5.20 GPA
5.58 GPa 5.58 GPA
Flexural modulus 4.53 GPa 4.53 GPA
4.58 GPa 4.58 GPA
Flexural yield strength 98.0 MPa 98.0 MPa
99.0 MPa 99.0 MPa
Simply supported beam impact, notch 0.500 J / cm² 0.500 J / cm2
Beam notched impact strength 0.550 J / cm 0.550 J / cm
0.690 J / cm 0.690 J / cm
Beam notched impact strength, notched (ISO) 5.00 kJ / m² 5.00 kJ / m2
5.00 kJ / m² 5.00 kJ / m2
Thermal performance Metric male
Coefficient of thermal expansion, linear, parallel flow 42.0 µm / m- ° C 42.0 μm / m- ° C
42.0 µm / m- ° C 42.0 μm / m- °-
Coefficient of thermal expansion, linear, lateral flow 49.0 µm / m- ° C 49.0 μm / m- ° C
59.0 μm / m- ° C 59.0 μm / m- ° C
Heat distortion temperature at 1.8 MPa (264 lbs) 89.0 ° C 89.0 ° C
88.0 ° C 88.0 ° C
Vicat softening point 107 ° C 107 ° C
108 ° C 108 ° C
110 ° C 110 ° C
Flammability, UL94 V-0 V-0
5VB 5VB

Working with Plastic Engine

You will get more mature professional engineering plastics supply services. We put customers first, and also actively challenge, and strive to present the best service quality to our customers.

Engineering Plastics Hotline:

400-6700-720
020-38937005

About Plastic Engine:
AG真人网 真人斗牛app 电玩竞技游戏 真人斗牛app 电玩游戏平台 电玩竞技游戏 皇冠体育官网 博狗直营