Sabic Lexan PC EXL9330-BK1A068

2016-11-14 09:20

Lexan PC EXL9330

-60 ℃ ductility, UV stability. Flame resistance V-0 / 5VA. Non-halogenated, bromine-free.

Property

(1) TYPICAL PROPERTIES (1)
MECHANICAL
Value Unit Standard
Tensile Stress, yld, Type I, 50 mm / min
590
kgf / cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm / min
620
kgf / cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm / min
6
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm / min
130
%
ASTM D 638
Tensile Modulus, 50 mm / min
21400
kgf / cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm / min, 50 mm span
900
kgf / cm2
ASTM D 790
Flexural Modulus, 1.3 mm / min, 50 mm span
21000
kgf / cm2
ASTM D 790
Tensile Stress, yield, 50 mm / min
55
MPa
ISO 527
Tensile Stress, break, 50 mm / min
60
MPa
ISO 527
Tensile Strain, yield, 50 mm / min
6
%
ISO 527
Tensile Strain, break, 50 mm / min
125
%
ISO 527
Tensile Modulus, 1 mm / min
2100
MPa
ISO 527
Flexural Stress, yield, 2 mm / min
85
MPa
ISO 178
Flexural Modulus, 2 mm / min
2200
MPa
ISO 178
Hardness, H358 / 30
90
MPa
ISO 2039-1
IMPACT
Value Unit Standard
Izod Impact, notched, 23 ° C
81
cm-kgf / cm
ASTM D 256
Izod Impact, notched, -30 ° C
69
cm-kgf / cm
ASTM D 256
Izod Impact, notched, -50 ° C
59
cm-kgf / cm
ASTM D 256
Izod Impact, notched, 23 ° C, 6.4mm
65
cm-kgf / cm
ASTM D 256
Izod Impact, double-gated, 23 ° C
108
cm-kgf / cm
SABIC Method
Instrumented Impact Total Energy, 23 ° C
539
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80 * 10 * 3 + 23 ° C
NB
kJ / m2
ISO 180 / 1U
Izod Impact, unnotched 80 * 10 * 3 -30 ° C
NB
kJ / m2
ISO 180 / 1U
Izod Impact, notched 80 * 10 * 3 + 23 ° C
70
kJ / m2
ISO 180 / 1A
Izod Impact, notched 80 * 10 * 3 -30 ° C
55
kJ / m2
ISO 180 / 1A
Izod Impact, notched 63.5 * 12.7 * 3.2, 23 ° C
80
kJ / m2
ISO 180 / 4A
Izod Impact, notched 63.5 * 12.7 * 3.2, -30 ° C
65
kJ / m2
ISO 180 / 4A
Charpy 23 ° C, V-notch Edgew 80 * 10 * 3 sp = 62mm
75
kJ / m2
ISO 179 / 1eA
Charpy -30 ° C, V-notch Edgew 80 * 10 * 3 sp = 62mm
60
kJ / m2
ISO 179 / 1eA
Charpy 23 ° C, Unnotch Edgew 80 * 10 * 3 sp = 62mm
NB
kJ / m2
ISO 179 / 1eU
Charpy -30 ° C, Unnotch Edgew 80 * 10 * 3 sp = 62mm
NB
kJ / m2
ISO 179 / 1eU
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B / 50
142
° C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
134
° C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
120
° C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
124
° C
ASTM D 648
CTE, -40 ° C to 40 ° C, flow
6.66E-05
1 / ° C
ASTM E 831
CTE, -40 ° C to 40 ° C, xflow
6.66E-05
1 / ° C
ASTM E 831
CTE, 23 ° C to 80 ° C, flow
7.2E-05
1 / ° C
ISO 11359-2
CTE, 23 ° C to 80 ° C, xflow
7.7E-05
1 / ° C
ISO 11359-2
Ball Pressure Test, 125 ° C +/- 2 ° C
PASSES
-
IEC 60695-10-2
Vicat Softening Temp, Rate B / 50
140
° C
ISO 306
Vicat Softening Temp, Rate B / 120
142
° C
ISO 306
HDT / Be, 0.45MPa Edgew 120 * 10 * 4 sp = 100mm
135
° C
ISO 75 / Be
HDT / Ae, 1.8 MPa Edgew 120 * 10 * 4 sp = 100mm
124
° C
ISO 75 / Ae
Relative Temp Index, Elec
125
° C
UL 746B
Relative Temp Index, Mech w / impact
115
° C
UL 746B
Relative Temp Index, Mech w / o impact
120
° C
UL 746B
PHYSICAL
Value Unit Standard
Specific Gravity
1.18
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm
0.4-0.8
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm
0.4-0.8
%
SABIC Method
Melt Flow Rate, 300 ° C / 1.2 kgf
10
g / 10 min
ASTM D 1238
Density
1.19
g / cm2
ISO 1183
Water Absorption, (23 ° C / sat)
0.35
%
ISO 62
Moisture Absorption (23 ° C / 50% RH)
0.15
%
ISO 62
Melt Volume Rate, MVR at 300 ° C / 1.2 kg
9
cm210 min
ISO 1133
ELECTRICAL
Value Unit Standard
Dielectric Strength, in oil, 3.2 mm
17
kV / mm
ASTM D 149
Relative Permittivity, 50/60 Hz
2.95
-
ASTM D 150
Relative Permittivity, 1 MHz
2.9
-
ASTM D 150
Dissipation Factor, 50/60 Hz
0.0024
-
ASTM D 150
Dissipation Factor, 1 MHz
0.0085
-
ASTM D 150
Hot Wire Ignition {PLC)
1
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
0
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
3
PLC Code
UL 746A
Volume Resistivity
> 1.E + 15
Ohm-cm
IEC 60093
Surface Resistivity, ROA
> 1.E + 15
Ohm
IEC 60093
Dielectric Strength, in oil, 3.2 mm
16
kV / mm
IEC 60243-1
Relative Permittivity, 50/60 Hz
2.6
-
IEC 60250
Relative Permittivity, 1 MHz
2.7
-
IEC 60250
Dissipation Factor, 50/60 Hz
0.001
-
IEC 60250
Dissipation Factor, 1 MHz
0.008
-
IEC 60250
Comparative Tracking Index
225
V
IEC 60112
FLAME CHARACTERISTICS
Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3)
1.49
mm
UL 94
UL Recognized, 94-5VA Rating (3)
2.99
mm
UL 94
Glow Wire Flammability Index 960 ° C, passes at
1
mm
IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm
825
° C
IEC 60695-2-13
Oxygen Index (LOI)
35
%
ISO 4589
UV-light, water exposure / immersion
F1
-
UL 746C

Processing

Parameter
Injection Molding
Value Unit
Drying Temperature
120
° C
Drying Time
3-4
hrs
Drying Time (Cumulative)
48
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
295-315
° C
Nozzle Temperature
290-310
° C
Front-Zone 3 Temperature
295-315
° C
Middle-Zone 2 Temperature
280-305
° C
Rear-Zone 1 Temperature
215-295
° C
Mold Temperature
70-95
° C
Back Pressure
0.3-0.7
MPa
Screw Speed
40-70
rpm
Shot to Cylinder Size
40-60
%
Vent Depth
0.025-0.076
mm

Working with Plastic Engine

You will get more mature professional engineering plastics supply services. We put customers first, and also actively challenge, and strive to present the best service quality to our customers.

Engineering Plastics Hotline:

400-6700-720
020-38937005

About Plastic Engine:
AG真人网 真人斗牛app 电玩竞技游戏 真人斗牛app 电玩游戏平台 电玩竞技游戏 皇冠体育官网 博狗直营